| Safonol | Gradd | ||||||
|---|---|---|---|---|---|---|---|
| Cyfansoddiad cemegol | |||||||
| C: | Ie: | Mn: | C: | S: | Cr: | Na chwaith: | Cu: |
| PN | 3PM | ||||||
| 0.12-0.18 | 0.17-0.37 | 0.5-0.8 | <0.035 | <0.035 | 0.7-1.0 | <0.3 | - |
| YN | 15Cr2 | ||||||
| 0.12-0.18 | 0.15-0.40 | 0.4-0.6 | <0.035 | <0.035 | 0.4-0.7 | - | - |
| YN | 17Cr3/1.7016 | ||||||
| 0.14-0.20 | <0.4 | 0.6-0.9 | <0.025 | <0.035 | 0.7-1.0 | - | - |
| Mae N.F. | 12C3 | ||||||
| 0.09-0.15 | <0,4 | 0.6-0.9 | <0,04 | <0.035 | 0.6-1.0 | - | - |
| JIS | SCr415 | ||||||
| 0.13-0.18 | 0.15-0.35 | 0.6-0.9 | <0,030 | <0,030 | 0.9-1.2 | <0,25 | <0,3 |
| GOST | 15Ch | ||||||
| 0.12-0.18 | 0.17-0.37 | 0.4-0.7 | <0,035 | <0,035 | 0.7-1.0 | <0,3 | <0,3 |
| UNE | F-1516 | ||||||
| 0.14-0.19 | <0,4 | 1.0-1.3 | <0,025 | <0,035 | 0.7-0.9 | - | - |
15H, 17Cr3, 15Cr3 - disgrifiad
Dur ar gyfer rhannau peiriant â gofynion cryfder isel, er enghraifft gwerthydau, pinnau, camsiafftau a llwyni. Dur y gellir ei weldio, y gellir ei beiriant a'i dorri. Weldio dim ond cyn carburizing. Mae'r dur yn debyg i 20Cr4 ond mae ganddo briodweddau mecanyddol israddol.
Priodweddau ffisegol a mecanyddol
Yma gallwch ddod o hyd i briodweddau mecanyddol yr aloion a ddewiswyd. Er gwaethaf eu tebygrwydd, maent yn amlwg yn wahanol.
| Priodweddau | Gradd | |||||
|---|---|---|---|---|---|---|
| PN | YN | YN | GOST | ČSN | ||
| 3PM | 15Cr3 | 17Cr3 | 15Ch | 14120 | ||
| Diamedr: | d | 15mm | 30mm | 10mm | 15mm | 30mm |
| Gwrthwynebiad i drosglwyddo: | Par | >490MPa | >390MPa | - | >490MPa | >343MPa |
| Cryfder tynnol: | RM | >690MPa | 590-880MPa | < 620 MPa | >686MPa | >588 MPa |
| Estyniad: | A5 | 12% | 14% | - | 12% | 14% |
| Gwrthiant effaith KCU, 20 gradd | KCU2 | 70 J/cm2 | - | - | 69 J/cm2 | R{0}} J/cm2 |
| Caledwch ar ôl anelio: | Mae H.B. | < 179 HB | < 202 HB | < 174 HB | 140-187 HB | < 155 HB |
Priodweddau Mecanyddol Forgings 15Ch
Trwch: <100mm
Cryfder tynnol > 345 MPa
Cryfder tynnol Rm: > 590 MPa
Elongation A: > 18%
Caledwch: 174-217
Gwerth effaith HB KCU: > 59 J/m2
Canran gostyngiad ardal Z: > 45%.
Trwch: 100-300mm
Cryfder tynnol > 345 MPa
Cryfder tynnol Rm: > 590 MPa
Elongation A: > 17%
Caledwch: 174-217 HB
Gwerth effaith KCU: > 54 J/m2
Canran gostyngiad ardal Z: > 40%.
Trwch: 5-10mm
Cryfder tynnol > 345 MPa
Cryfder tynnol Rm: > 590 MPa
Elongation A: > 14%
Caledwch: 174-217 HB
Gwerth effaith KCU: > 49 J/m2
Canran gostyngiad ardal Z: > 38%.
Trwch: 5-10mm
Cryfder tynnol > 345 MPa
Cryfder tynnol Rm: > 590 MPa
Elongation A: > 12%
Caledwch: 174-217 HB
Gwerth effaith KCU: > 39 J/m2
Canran gostyngiad ardal Z: > 33%.
Priodweddau mecanyddol tiwbiau 15Ch
Trwch wal: <10mm
Cryfder tynnol Rm: > 412 MPa
Elongation A: > 19%
Trwch wal: > 10mm
Cryfder tynnol Rm: > 412 MPa
Elongation A: > 19%
Caledwch < 179 HB
Bariau, stribedi a choiliau Rodiau Gwifrau Platiau